Cross-linked Cellulose Nanocrystal Aerogels as Viable Bone Tissue Scaffolds

Chemically cross-linked cellulose nanocrystal (CNC) aerogels possess many properties beneficial for bone tissue scaffolding applications. CNCs were extracted using sulfuric acid or phosphoric acid, to produce CNCs with sulfate and phosphate half-ester surface groups, respectively. Hydrazone cross-linked aerogels fabricated from the two types of CNCs were investigated using scanning electron microscopy, X-ray micro-computed tomography, X-ray photoelectron spectroscopy, nitrogen sorption isotherms, and compression testing. CNC aerogels were evaluated in vitro with osteoblast-like, Saos-2, cells and showed an increase in cell metabolism up to 7 days while alkaline phosphatase assays revealed that Saos-2 cells maintained their phenotype. All aerogels demonstrated hydroxyapatite growth over 14 days while submerged in simulated body fluid solution with a 0.1 M CaCl2 pre-treatment. Sulfated CNC aerogels slightly outperformed phosphated CNC aerogels in terms of compressive strength and long-term stability in liquid environments, and were implanted into the calvarian bone of adult male Long Evans rats. Compared to controls at 3 and 12 week time points, sulfated CNC aerogels showed increased bone volume fraction of 33% and 50%, respectively, compared to controls, and evidence of osteoconductivity. These results demonstrate that cross-linked CNC aerogels are flexible, porous and effectively facilitate bone growth after they are implanted in bone defects.